Effect of blue and violet light on polymerization shrinkage vectors of a CQ/TPO-containing composite

Camila S. Sampaio, Pablo J. Atria, Frederick Rueggeberg, Satoshi Yamaguchi, Marcelo Giannini, Paulo G. Coelho, Ronaldo Hirata, Regina M. Puppin-Rontani

Research output: Contribution to journalArticle

6 Citations (Scopus)

Abstract

Objective To evaluate the effect of light-curing wavelengths on composite filler particle displacement, and thus to visualize localized polymerization shrinkage in a resin-based composite (RBC) containing camphorquinone (CQ) and Lucirin TPO (TPO). Methods Three light-curing units (LCUs) were used to light-cure a RBC containing CQ and TPO: a violet-only, a blue-only, and a dual-wavelength, conventional (Polywave®, emitting violet and blue wavelengths simultaneously). Zirconia fillers were added to the RBC to act as filler particle displacement tracers. LCUs were characterized for total emitted power (mW) and spectral irradiant output (mW/cm2/nm). 2-mm high, 7-mm diameter silanized glass cylindrical specimens were filled in a single increment with the RBC, and micro-computed tomography (μ-CT) scans were obtained before and after light-curing, according to each LCU (n = 6). Filler particle movement identified polymerization shrinkage vectors, traced using software, at five depths (from 0 up to 2 mm): top, top-middle, middle, middle-bottom and bottom. Results Considering different RBC depths within the same LCU, use of violet-only and conventional LCUs showed filler particle movement decreased with increased depth. Blue-only LCU showed homogeneous filler particle movement along the depths. Considering the effect of different LCUs within the same depth, filler particle movement within LCUs was not statistically different until the middle of the samples (P > .05). However, at the middle-bottom and bottom depths (1.5 and 2 mm, respectively), blue-only LCU compared to violet-only LCU showed higher magnitude of displacement vector values (P < .05). Use of the conventional LCU showed filler displacement magnitudes that were not significantly different than blue-only and violet-only LCUs at any depth (P > .05). With respect to the direction of particle movement vectors, use of violet-only LCU showed a greater displacement when close to the incident violet LED; blue-only LCU showed equally distributed particle displacement values within entire depth among the samples; and the conventional LCU showed greater filler displacement closer to the blue LED locations. Significance Filler particle displacement in a RBC as a result of light-curing is related to localized application of light wavelength and total emitted power of the light emitted on the top surface of the RBC. When the violet LED is present (violet-only and conventional LCUs), filler particle displacement magnitude decreased with increased depth, while results using the blue-only LED show a more consistent pattern of displacement. Clinically, these results correlate to production of different characteristics of curing within a RBC restoration mass, depending on localized wavelengths applied to the irradiated surface.

Original languageEnglish (US)
Pages (from-to)796-804
Number of pages9
JournalDental Materials
Volume33
Issue number7
DOIs
StatePublished - Jul 1 2017

Fingerprint

Polymerization
Curing
Light
Composite materials
Composite Resins
Fillers
Viola
Resins
Light emitting diodes
Wavelength
camphorquinone

Keywords

  • Dental curing lights
  • Light emitting diode
  • Micro-computed tomography
  • Non-destructive image
  • Photopolymerization
  • Polymerization shrinkage vectors

ASJC Scopus subject areas

  • Materials Science(all)
  • Dentistry(all)
  • Mechanics of Materials

Cite this

Sampaio, C. S., Atria, P. J., Rueggeberg, F., Yamaguchi, S., Giannini, M., Coelho, P. G., ... Puppin-Rontani, R. M. (2017). Effect of blue and violet light on polymerization shrinkage vectors of a CQ/TPO-containing composite. Dental Materials, 33(7), 796-804. https://doi.org/10.1016/j.dental.2017.04.010

Effect of blue and violet light on polymerization shrinkage vectors of a CQ/TPO-containing composite. / Sampaio, Camila S.; Atria, Pablo J.; Rueggeberg, Frederick; Yamaguchi, Satoshi; Giannini, Marcelo; Coelho, Paulo G.; Hirata, Ronaldo; Puppin-Rontani, Regina M.

In: Dental Materials, Vol. 33, No. 7, 01.07.2017, p. 796-804.

Research output: Contribution to journalArticle

Sampaio, CS, Atria, PJ, Rueggeberg, F, Yamaguchi, S, Giannini, M, Coelho, PG, Hirata, R & Puppin-Rontani, RM 2017, 'Effect of blue and violet light on polymerization shrinkage vectors of a CQ/TPO-containing composite', Dental Materials, vol. 33, no. 7, pp. 796-804. https://doi.org/10.1016/j.dental.2017.04.010
Sampaio, Camila S. ; Atria, Pablo J. ; Rueggeberg, Frederick ; Yamaguchi, Satoshi ; Giannini, Marcelo ; Coelho, Paulo G. ; Hirata, Ronaldo ; Puppin-Rontani, Regina M. / Effect of blue and violet light on polymerization shrinkage vectors of a CQ/TPO-containing composite. In: Dental Materials. 2017 ; Vol. 33, No. 7. pp. 796-804.
@article{493fc2898ae844d99a2d6f018e7804d6,
title = "Effect of blue and violet light on polymerization shrinkage vectors of a CQ/TPO-containing composite",
abstract = "Objective To evaluate the effect of light-curing wavelengths on composite filler particle displacement, and thus to visualize localized polymerization shrinkage in a resin-based composite (RBC) containing camphorquinone (CQ) and Lucirin TPO (TPO). Methods Three light-curing units (LCUs) were used to light-cure a RBC containing CQ and TPO: a violet-only, a blue-only, and a dual-wavelength, conventional (Polywave{\circledR}, emitting violet and blue wavelengths simultaneously). Zirconia fillers were added to the RBC to act as filler particle displacement tracers. LCUs were characterized for total emitted power (mW) and spectral irradiant output (mW/cm2/nm). 2-mm high, 7-mm diameter silanized glass cylindrical specimens were filled in a single increment with the RBC, and micro-computed tomography (μ-CT) scans were obtained before and after light-curing, according to each LCU (n = 6). Filler particle movement identified polymerization shrinkage vectors, traced using software, at five depths (from 0 up to 2 mm): top, top-middle, middle, middle-bottom and bottom. Results Considering different RBC depths within the same LCU, use of violet-only and conventional LCUs showed filler particle movement decreased with increased depth. Blue-only LCU showed homogeneous filler particle movement along the depths. Considering the effect of different LCUs within the same depth, filler particle movement within LCUs was not statistically different until the middle of the samples (P > .05). However, at the middle-bottom and bottom depths (1.5 and 2 mm, respectively), blue-only LCU compared to violet-only LCU showed higher magnitude of displacement vector values (P < .05). Use of the conventional LCU showed filler displacement magnitudes that were not significantly different than blue-only and violet-only LCUs at any depth (P > .05). With respect to the direction of particle movement vectors, use of violet-only LCU showed a greater displacement when close to the incident violet LED; blue-only LCU showed equally distributed particle displacement values within entire depth among the samples; and the conventional LCU showed greater filler displacement closer to the blue LED locations. Significance Filler particle displacement in a RBC as a result of light-curing is related to localized application of light wavelength and total emitted power of the light emitted on the top surface of the RBC. When the violet LED is present (violet-only and conventional LCUs), filler particle displacement magnitude decreased with increased depth, while results using the blue-only LED show a more consistent pattern of displacement. Clinically, these results correlate to production of different characteristics of curing within a RBC restoration mass, depending on localized wavelengths applied to the irradiated surface.",
keywords = "Dental curing lights, Light emitting diode, Micro-computed tomography, Non-destructive image, Photopolymerization, Polymerization shrinkage vectors",
author = "Sampaio, {Camila S.} and Atria, {Pablo J.} and Frederick Rueggeberg and Satoshi Yamaguchi and Marcelo Giannini and Coelho, {Paulo G.} and Ronaldo Hirata and Puppin-Rontani, {Regina M.}",
year = "2017",
month = "7",
day = "1",
doi = "10.1016/j.dental.2017.04.010",
language = "English (US)",
volume = "33",
pages = "796--804",
journal = "Dental Materials",
issn = "0109-5641",
publisher = "Elsevier Science",
number = "7",

}

TY - JOUR

T1 - Effect of blue and violet light on polymerization shrinkage vectors of a CQ/TPO-containing composite

AU - Sampaio, Camila S.

AU - Atria, Pablo J.

AU - Rueggeberg, Frederick

AU - Yamaguchi, Satoshi

AU - Giannini, Marcelo

AU - Coelho, Paulo G.

AU - Hirata, Ronaldo

AU - Puppin-Rontani, Regina M.

PY - 2017/7/1

Y1 - 2017/7/1

N2 - Objective To evaluate the effect of light-curing wavelengths on composite filler particle displacement, and thus to visualize localized polymerization shrinkage in a resin-based composite (RBC) containing camphorquinone (CQ) and Lucirin TPO (TPO). Methods Three light-curing units (LCUs) were used to light-cure a RBC containing CQ and TPO: a violet-only, a blue-only, and a dual-wavelength, conventional (Polywave®, emitting violet and blue wavelengths simultaneously). Zirconia fillers were added to the RBC to act as filler particle displacement tracers. LCUs were characterized for total emitted power (mW) and spectral irradiant output (mW/cm2/nm). 2-mm high, 7-mm diameter silanized glass cylindrical specimens were filled in a single increment with the RBC, and micro-computed tomography (μ-CT) scans were obtained before and after light-curing, according to each LCU (n = 6). Filler particle movement identified polymerization shrinkage vectors, traced using software, at five depths (from 0 up to 2 mm): top, top-middle, middle, middle-bottom and bottom. Results Considering different RBC depths within the same LCU, use of violet-only and conventional LCUs showed filler particle movement decreased with increased depth. Blue-only LCU showed homogeneous filler particle movement along the depths. Considering the effect of different LCUs within the same depth, filler particle movement within LCUs was not statistically different until the middle of the samples (P > .05). However, at the middle-bottom and bottom depths (1.5 and 2 mm, respectively), blue-only LCU compared to violet-only LCU showed higher magnitude of displacement vector values (P < .05). Use of the conventional LCU showed filler displacement magnitudes that were not significantly different than blue-only and violet-only LCUs at any depth (P > .05). With respect to the direction of particle movement vectors, use of violet-only LCU showed a greater displacement when close to the incident violet LED; blue-only LCU showed equally distributed particle displacement values within entire depth among the samples; and the conventional LCU showed greater filler displacement closer to the blue LED locations. Significance Filler particle displacement in a RBC as a result of light-curing is related to localized application of light wavelength and total emitted power of the light emitted on the top surface of the RBC. When the violet LED is present (violet-only and conventional LCUs), filler particle displacement magnitude decreased with increased depth, while results using the blue-only LED show a more consistent pattern of displacement. Clinically, these results correlate to production of different characteristics of curing within a RBC restoration mass, depending on localized wavelengths applied to the irradiated surface.

AB - Objective To evaluate the effect of light-curing wavelengths on composite filler particle displacement, and thus to visualize localized polymerization shrinkage in a resin-based composite (RBC) containing camphorquinone (CQ) and Lucirin TPO (TPO). Methods Three light-curing units (LCUs) were used to light-cure a RBC containing CQ and TPO: a violet-only, a blue-only, and a dual-wavelength, conventional (Polywave®, emitting violet and blue wavelengths simultaneously). Zirconia fillers were added to the RBC to act as filler particle displacement tracers. LCUs were characterized for total emitted power (mW) and spectral irradiant output (mW/cm2/nm). 2-mm high, 7-mm diameter silanized glass cylindrical specimens were filled in a single increment with the RBC, and micro-computed tomography (μ-CT) scans were obtained before and after light-curing, according to each LCU (n = 6). Filler particle movement identified polymerization shrinkage vectors, traced using software, at five depths (from 0 up to 2 mm): top, top-middle, middle, middle-bottom and bottom. Results Considering different RBC depths within the same LCU, use of violet-only and conventional LCUs showed filler particle movement decreased with increased depth. Blue-only LCU showed homogeneous filler particle movement along the depths. Considering the effect of different LCUs within the same depth, filler particle movement within LCUs was not statistically different until the middle of the samples (P > .05). However, at the middle-bottom and bottom depths (1.5 and 2 mm, respectively), blue-only LCU compared to violet-only LCU showed higher magnitude of displacement vector values (P < .05). Use of the conventional LCU showed filler displacement magnitudes that were not significantly different than blue-only and violet-only LCUs at any depth (P > .05). With respect to the direction of particle movement vectors, use of violet-only LCU showed a greater displacement when close to the incident violet LED; blue-only LCU showed equally distributed particle displacement values within entire depth among the samples; and the conventional LCU showed greater filler displacement closer to the blue LED locations. Significance Filler particle displacement in a RBC as a result of light-curing is related to localized application of light wavelength and total emitted power of the light emitted on the top surface of the RBC. When the violet LED is present (violet-only and conventional LCUs), filler particle displacement magnitude decreased with increased depth, while results using the blue-only LED show a more consistent pattern of displacement. Clinically, these results correlate to production of different characteristics of curing within a RBC restoration mass, depending on localized wavelengths applied to the irradiated surface.

KW - Dental curing lights

KW - Light emitting diode

KW - Micro-computed tomography

KW - Non-destructive image

KW - Photopolymerization

KW - Polymerization shrinkage vectors

UR - http://www.scopus.com/inward/record.url?scp=85019400351&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85019400351&partnerID=8YFLogxK

U2 - 10.1016/j.dental.2017.04.010

DO - 10.1016/j.dental.2017.04.010

M3 - Article

VL - 33

SP - 796

EP - 804

JO - Dental Materials

JF - Dental Materials

SN - 0109-5641

IS - 7

ER -