Thermal properties of a methyl methacrylate-based orthodontic bonding adhesive

Frederick Rueggeberg, Felix T. Maher, Michael T. Kelly

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

Methyl methacrylate-based (MMA-based) bonding resins have been used in orthodontics because they offer easy removal of both the bonded bracket and the residual adhesive at case completion. However, these materials are not cross-linked, and the brackets bonded with this type of product may undergo drifting when subjected to temperatures slightly higher than those in the mouth. This research investigated the influence of heat on the debonding characteristics of a MMA-based bonding resin compared with those of a BIS-GMA-based system. The temperature of initial bracket movement, as well as of final bracket displacement, was noted for a variety of applied loads (141, 226, 425, 934, and 1727 gm) with stainless steel brackets bonded to etched bovine enamel. The results showed that the MMA-based material underwent a glass transition near 47°C in which the initiation of bracket drift resulted on the tooth surface. This temperature proved independent of the applied load. Further heating resulted in the release of heat from the resin as a result of further curing. The extent of bracket drift associated with this secondary heat release was dependent on the applied load. The debonding temperature of the BIS-GMA-based system was three to six times greater than that of the MMA-based product. Practitioners should be aware that brackets bonded with MMA-based resins have the potential for drifting when subjected to temperatures within the normal range of hot fluids consumed by their patients. Bracket drift could result in deactivation of orthodontic force and could prolong the treatment time.

Original languageEnglish (US)
Pages (from-to)342-349
Number of pages8
JournalAmerican Journal of Orthodontics and Dentofacial Orthopedics
Volume101
Issue number4
DOIs
StatePublished - Jan 1 1992
Externally publishedYes

Fingerprint

Dental Cements
Methacrylates
Hot Temperature
Temperature
Orthodontics
Stainless Steel
Dental Enamel
Adhesives
Heating
Glass
Mouth
Tooth
Reference Values
Research

ASJC Scopus subject areas

  • Orthodontics

Cite this

Thermal properties of a methyl methacrylate-based orthodontic bonding adhesive. / Rueggeberg, Frederick; Maher, Felix T.; Kelly, Michael T.

In: American Journal of Orthodontics and Dentofacial Orthopedics, Vol. 101, No. 4, 01.01.1992, p. 342-349.

Research output: Contribution to journalArticle

@article{e1298b1f15b74c609a53941b6bede8fc,
title = "Thermal properties of a methyl methacrylate-based orthodontic bonding adhesive",
abstract = "Methyl methacrylate-based (MMA-based) bonding resins have been used in orthodontics because they offer easy removal of both the bonded bracket and the residual adhesive at case completion. However, these materials are not cross-linked, and the brackets bonded with this type of product may undergo drifting when subjected to temperatures slightly higher than those in the mouth. This research investigated the influence of heat on the debonding characteristics of a MMA-based bonding resin compared with those of a BIS-GMA-based system. The temperature of initial bracket movement, as well as of final bracket displacement, was noted for a variety of applied loads (141, 226, 425, 934, and 1727 gm) with stainless steel brackets bonded to etched bovine enamel. The results showed that the MMA-based material underwent a glass transition near 47°C in which the initiation of bracket drift resulted on the tooth surface. This temperature proved independent of the applied load. Further heating resulted in the release of heat from the resin as a result of further curing. The extent of bracket drift associated with this secondary heat release was dependent on the applied load. The debonding temperature of the BIS-GMA-based system was three to six times greater than that of the MMA-based product. Practitioners should be aware that brackets bonded with MMA-based resins have the potential for drifting when subjected to temperatures within the normal range of hot fluids consumed by their patients. Bracket drift could result in deactivation of orthodontic force and could prolong the treatment time.",
author = "Frederick Rueggeberg and Maher, {Felix T.} and Kelly, {Michael T.}",
year = "1992",
month = "1",
day = "1",
doi = "10.1016/S0889-5406(05)80327-0",
language = "English (US)",
volume = "101",
pages = "342--349",
journal = "American Journal of Orthodontics and Dentofacial Orthopedics",
issn = "0889-5406",
publisher = "Mosby Inc.",
number = "4",

}

TY - JOUR

T1 - Thermal properties of a methyl methacrylate-based orthodontic bonding adhesive

AU - Rueggeberg, Frederick

AU - Maher, Felix T.

AU - Kelly, Michael T.

PY - 1992/1/1

Y1 - 1992/1/1

N2 - Methyl methacrylate-based (MMA-based) bonding resins have been used in orthodontics because they offer easy removal of both the bonded bracket and the residual adhesive at case completion. However, these materials are not cross-linked, and the brackets bonded with this type of product may undergo drifting when subjected to temperatures slightly higher than those in the mouth. This research investigated the influence of heat on the debonding characteristics of a MMA-based bonding resin compared with those of a BIS-GMA-based system. The temperature of initial bracket movement, as well as of final bracket displacement, was noted for a variety of applied loads (141, 226, 425, 934, and 1727 gm) with stainless steel brackets bonded to etched bovine enamel. The results showed that the MMA-based material underwent a glass transition near 47°C in which the initiation of bracket drift resulted on the tooth surface. This temperature proved independent of the applied load. Further heating resulted in the release of heat from the resin as a result of further curing. The extent of bracket drift associated with this secondary heat release was dependent on the applied load. The debonding temperature of the BIS-GMA-based system was three to six times greater than that of the MMA-based product. Practitioners should be aware that brackets bonded with MMA-based resins have the potential for drifting when subjected to temperatures within the normal range of hot fluids consumed by their patients. Bracket drift could result in deactivation of orthodontic force and could prolong the treatment time.

AB - Methyl methacrylate-based (MMA-based) bonding resins have been used in orthodontics because they offer easy removal of both the bonded bracket and the residual adhesive at case completion. However, these materials are not cross-linked, and the brackets bonded with this type of product may undergo drifting when subjected to temperatures slightly higher than those in the mouth. This research investigated the influence of heat on the debonding characteristics of a MMA-based bonding resin compared with those of a BIS-GMA-based system. The temperature of initial bracket movement, as well as of final bracket displacement, was noted for a variety of applied loads (141, 226, 425, 934, and 1727 gm) with stainless steel brackets bonded to etched bovine enamel. The results showed that the MMA-based material underwent a glass transition near 47°C in which the initiation of bracket drift resulted on the tooth surface. This temperature proved independent of the applied load. Further heating resulted in the release of heat from the resin as a result of further curing. The extent of bracket drift associated with this secondary heat release was dependent on the applied load. The debonding temperature of the BIS-GMA-based system was three to six times greater than that of the MMA-based product. Practitioners should be aware that brackets bonded with MMA-based resins have the potential for drifting when subjected to temperatures within the normal range of hot fluids consumed by their patients. Bracket drift could result in deactivation of orthodontic force and could prolong the treatment time.

UR - http://www.scopus.com/inward/record.url?scp=0026846686&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0026846686&partnerID=8YFLogxK

U2 - 10.1016/S0889-5406(05)80327-0

DO - 10.1016/S0889-5406(05)80327-0

M3 - Article

VL - 101

SP - 342

EP - 349

JO - American Journal of Orthodontics and Dentofacial Orthopedics

JF - American Journal of Orthodontics and Dentofacial Orthopedics

SN - 0889-5406

IS - 4

ER -